A microscopia eletrônica de varredura pode ser usada para medir quantitativamente a rugosidade da dentina? / Can Scanning Electron Microscopy be used to quantitatively measure dentine roughness?

Objective: The aim of this study was to determine if SEM used with imaging software could be used to quantitatively determine the extent of dentine roughness due to tooth-brushing. Material and methods: Flat, polished dentine surfaces were subjected to 25,000 cycles of simulated tooth-brushing at 2 strokes per second with a load of 200 g. At the end of the brushing cycle, dentine surfaces were first assessed using profilometry and then subjected to SEM analysis. Ra (average roughness) readings were obtained for profilometric assessment. Using imaging software, the horizontal distance between adjacent characteristic grooves noted on micrographs was measured, ensuring that the middle of each crest of the associated groove was used as the reference point, the Crest-to-Crest distance (C-C distance). These two parameters were examined statistically for correlation. Results: When Spearman Rank tests were utilized the correlation between average Ra and crest to crest measurements was 0.709 (p <0.01). The Bland Altman plot, however, showed poor agreement between the two test parameters. Conclusion: Further work is needed to validate the use of this methodology in the quantitative assessment of tooth surface loss due to abrasion (AU)

Objetivo: O objetivo deste estudo foi determinar se o MEV usado com software de imagem poderia ser usado para determinar quantitativamente a extensão da rugosidade da dentina devido à escovação dentária. Material e Métodos: Superfícies dentinárias planas e polidas foram submetidas a 25.000 ciclos de escovação dentária simulada a 2 movimentos por segundo com uma carga de 200g. No final do ciclo de escovação, as superfícies dentinárias foram primeiro avaliadas por perfilometria e depois submetidas à análise MEV. Leituras de Ra (rugosidade média) foram obtidas para avaliação perfilométrica. Utilizando um software de imagem, foi medida a distância horizontal entre sulcos característicos adjacentes observados nas micrografias, garantindo que o meio de cada crista do sulco associado fosse usado como ponto de referência, a distância crista a crista (distância CC). Esses dois parâmetros foram examinados estatisticamente para correlação. Resultados: Quando foram utilizados os testes de Spearman Rank, a correlação entre a média de Ra e as medidas de crista a crista foi de 0,709 (p<0,01). O gráfico de Bland Altman, no entanto, mostrou fraca concordância entre os dois parâmetros de teste. Conclusão: Mais trabalhos são necessários para validar o uso desta metodologia na avaliação quantitativa da perda da superfície dentária devido à abrasão(AU)

Synthesis, characterization and protection effect of black rice anthocyanins nano-composite against hepatotoxicity induced by methotrexate in rats

Abstract The present study aimed to investigate the beneficial of prepared black rice anthocyanins nano-composite (An-AgNps) against hepatotoxicity induced by methotrexate (MTX) in rats. Anthocyanins nano-composite was prepared by silver as the metallic ion reduction and were characterized by IR and SEM. The rats in our experiment were divided into five groups. Serum lipid profile, serum transaminases (ALT and AST), ALP, LDH, TBA, GSH and SOD were examined. The results show that SEM of An-AgNps has average particle size from 70 to 130nm. In the group treated with MTX; TC, TG, LDL-c, ALT, AST, ALP, LDH and TBA levels were significantly (P0.05) increased than NC, while, HDL-c, SOD and GSH levels were significantly (P0.05) decreased. On the other hand, An-AgNps + MTX treated groups were reversed the levels of all biomarkers similar to NC. In conclusion, the results show that An-AgNps has a protective effect on MTX-induced hepatotoxicity and oxidative stress.

Resumo O presente estudo teve como objetivo investigar o benefício de nanocompósito de antocianinas de arroz preto preparado (An-AgNps) contra a hepatotoxicidade induzida por metotrexato (MTX) em ratos. O nanocompósito de antocianinas foi preparado a partir da prata por meio da redução do íon metálico e caracterizado por IR e SEM. Os ratos em nosso experimento foram divididos em cinco grupos, e foram examinados o perfil lipídico sérico, as transaminases séricas (ALT e AST), ALP, LDH, TBA, GSH e SOD. Os resultados mostram que SEM de An-AgNps tem tamanho médio de partícula de 70 a 130 nm. No grupo tratado com MTX, os níveis de TC, TG, LDL-c, ALT, AST, ALP, LDH e TBA aumentaram significativamente (P 0,05) do que NC, enquanto os níveis de HDL-c, SOD e GSH diminuíram significativamente (P 0,05). Por outro lado, nos grupos tratados com An-AgNps + MTX, foram revertidos os níveis de todos os biomarcadores semelhantes ao NC. Em conclusão, os resultados mostram que o An-AgNps tem um efeito protetor contra a hepatotoxicidade induzida pelo MTX e o estresse oxidativo.

Avaliação dos Efeitos da Remoção da Resina Residual e do Polimento na Superfície do Esmalte após Descolagem do Braquete / Evaluation of the Effects of Residual Resin Removal and Polishing on the Enamel Surface after Bracket Debonding

Considerando o uso de brocas para remoção da resina residual após descolagem do braquete e a possibilidade de injúrias à superfície do esmalte após o uso dessas brocas, este trabalho teve como objetivo realizar um estudo experimental, para avaliar a variação do aspecto superficial do esmalte de forma qualitativa, por meio da avaliação com imagens topográficas do esmalte dentário, utilizando-se a Microscopia Eletrônica de Varredura (MEV), a qual permitiu ilustrar e avaliar a superfície do esmalte após a fase de polimento final, realizada por dois métodos: taça de borracha ou escova Robinson. Foram utilizados 25 dentes pré-molares humanos, obtidos a partir de exodontias em pacientes que procuraram voluntariamente o curso de Residência em Cirurgia da Clínica Odontológica Universitária da Universidade Estadual de Londrina. Os dentes foram divididos em quatro grupos: A, B, C e D, contendo 6 dentes cada, de acordo com as brocas utilizadas para a remoção do remanescente adesivo e o polimento escolhido, além de um dente como "controle". Foi avaliada a rugosidade superficial do esmalte após a remoção da resina e a superfície do esmalte após o polimento com as duas opções apresentadas. Os resultados mostraram que, por observação e inspeção, as brocas removeram a resina residual de todos os dentes, porém, causaram riscos e ranhuras, como evidenciado nas imagens em MEV. Concluiu-se que não houve diferença estatística entre os métodos de polimento e que ambos foram importantes para a redução das marcas abrasivas, proporcionando uma superfície mais lisa do esmalte.

Considering the use of specific burs to remove residual resin after bracket debonding and the possibility of injuries to the dental enamel after using these burs, this study aimed to verify the variation in the enamel surface appearance in a qualitative way and evaluation with topographic images of the dental enamel. The use of Scanning Electron Microscopy (SEM) allowed to illustrate and evaluate the enamel surface after the final polishing phase using two methods: rubber cup or Robinson brush. Twenty-five human premolar teeth were obtained from extractions in patients who voluntarily sought the Oral Maxillofacial Surgery Residency at the Dental School from the State University of Londrina; the teeth were divided into four groups A, B, C and D containing 6 teeth each according to the burs used to remove the remaining adhesive and the chosen polishing, in addition to one tooth as a "control". Dental enamel surface roughness was evaluated after resin removal and enamel surface after polishing with the two methods presented. The results showed that by observation and inspection, the burs removed residual resin from all teeth, however, caused scratches and grooves as evidenced in the SEM images. Based on the results, there was no statistical difference between the polishing methods, and both were important for the reduction of abrasive marks and provided a smoother enamel surface.

Analysis of biofilm formation by Candida albicans in different types of orthodontic fixed appliances and devices / Análise da formação de biofilme por Candida albicans em diferentes tipos de aparelhos e dispositivos ortodônticos fixos

Objective: in this study, biofilm formation by Candida albicans in fixed orthodontic appliances was evaluated. Material and Methods: a total of 300 conventional metal brackets (MC), ceramic (CB), self-ligation (SLB), nickel-titanium (NiTi), and nickel-chromium (NiCr) wires, and ligatures types were organized into thirty groups (n=10). To induce biofilm formation, brackets, wires, and ligatures were joined, sterilized, placed in 24-well plates, contaminated with standardized suspensions of C. albicans (107 cells/mL), and incubated at 37 °C for 48 h with shaking. The biofilms formed were detached using an ultrasonic homogenizer, and suspensions were serially diluted and plated on Sabouraud dextrose agar to determine colony-forming units per mL. Scanning electron microscopy was performed before and after the biofilm formation. Results: lower amount of biofilm formation was observed in the MC group than in the CB and SLB groups (p<0.0001). SLB and CB showed similar biofilm formation rates (p=0.855). In general, the cross-sectional wires .018"x.025" showed higher biofilm formation when associated with the three types of brackets. When brackets, wires, and ligatures were associated, the sets with NiCr wires and SSL ligatures with MC brackets (p=0.0008) and CB (p=0.0003) showed higher biofilm formation. Conclusion: thus, brackets of MC with NiTi and NiCr wires showed lower biofilm formation, regardless of the ligature and cross-sectional or gauge of the wire and, MC and CB brackets with NiCr wires and SSL ligatures were more likely to accumulate biofilms (AU)

Objetivo: neste estudo, a formação de biofilme por Candida albicans em aparelhos ortodônticos fixos foi avaliada. Material e Métodos: um total de 300 bráquetes metálicos convencionais (MC), cerâmicos (CB), autoligados (SLB), com fios de níquel-titânio (NiTi) e níquel-cromo (NiCr) e tipos de ligaduras foram organizados em trinta grupos (n=10). Bráquetes, fios e ligaduras foram unidos, esterilizados, colocados em placas de 24 poços, contaminados com suspensões padronizadas de C. albicans (107 células/mL) e incubados a 37°C por 48 h para a formação de biofilmes. Os biofilmes formados foram rompidos por meio de um homogeneizador ultrassônico e suspensões foram diluídas e semeadas em ágar Sabouraud-dextrose para determinar as unidades formadoras de colônias por mL. A microscopia eletrônica de varredura foi realizada antes e após a formação do biofilme. Resultados: foi observada menor formação de biofilme no grupo MC em comparação aos grupos CB e SLB (p<0,0001). A formação de biofilme foi semelhante nos grupos SLB e CB (p=0,855). Em geral, os fios de seção transversal .018"x.025" apresentaram maior formação de biofilme quando associados aos três tipos de bráquetes. Os conjuntos com fios de NiCr e ligaduras SSL com bráquetes MC (p=0,0008) e CB (p=0,0003) apresentaram maior formação de biofilme. Conclusão: bráquetes MC com fios de NiTi e NiCr apresentaram menor formação de biofilme, independente da ligadura e secção transversal ou bitola do fio e, braquetes MC e CB com fios de NiCr e ligaduras SSL foram mais propensos a acumular biofilmes.(AU)

Bonding strategy of a universal adhesive system containing chitosan: influence on dentin permeability, and effect on adhesive layer micromorphology / Estratégia de união de um sistema adesivo universal contendo quitosana: influência na permeabilidade dentinária e efeito na micromorfologia da camada do adesivo

ABSTRACT Aim: This study evaluated the influence of chitosan added to a universal adhesive system used in totaletch (TE) or self-etch (SE) mode on dentin permeability, and on the micromorphology of the adhesive layer. Materials and Method: Dentin discs were obtained from human third molars and randomly distributed according to bonding strategy (TE or SE), and to whether or not 1% chitosan (C) was added to a universal adhesive system (Single Bond Universal/3M ESPE), to create the following groups (n=10): TE, TEC, SE, and SEC. Dentin permeability was measured at baseline and after application of dentin treatments. The surface of the adhesive layer (AL) and the dentin adjacent to the AL were examined under a scanning electron microscope. Results: There were no significant differences in permeability percentage between the groups with and without C (TE and SE versus TEC and SEC) (p>0.05; Mann Whitney test). Dentin permeability was lower when the adhesive system was applied in the SE mode, regardless of the addition of C. The micromorphology of the AL surface showed irregularities, and a greater degree of porosity, when the adhesive system was applied in the SE mode, regardless of chitosan addition. There was a greater depth of penetration of the adhesives into the dentin adjacent to the AL in both the TE and TEC groups. Chitosan added to the adhesive system did not influence dentin permeability. Conclusions: The self-etch strategy led to lower dentin permeability, and to more irregularities on the surface of the adhesive layer.

RESUMO Objetivo: Este estudo avaliou a influência da quitosana adicionada a um sistema adesivo universal usado no modo total-etch (TE) ou self-etch (SE) na permeabilidade dentinária e na micromorfologia da camada adesiva. Materiais e método: Discos de dentina foram obtidos de terceiros molares humanos e distribuídos aleatoriamente de acordo com a estratégia de união (TE ou SE), e para incorporação ou não de quitosana a 1% (Q) em um sistema adesivo universal (Single Bond Universal/3M ESPE), para obter os seguintes grupos (n=10): TE, TEQ, SE e SEQ. A permeabilidade da dentina foi medida no início e após a aplicação dos tratamentos de dentina. A superfície da camada adesiva (CA) e a dentina adjacente à CA foram examinadas em microscópio eletrônico de varredura. Resultados: Não houve diferenças significativas no percentual de permeabilidade entre os grupos com e sem Q (TE e SE versus TEQ e SEQ) (p>0,05; teste de Mann Whitney). Houve um menor percentual de permeabilidade dentinária quando o sistema adesivo foi aplicado no modo SE, independentemente da incorporação de Q. A micromorfologia da superfície da CA apresentou irregularidades e maior grau de porosidade quando o sistema adesivo foi aplicado no modo SE, independentemente da adição de Q. Houve maior profundidade de penetração dos adesivos na dentina adjacente à CA nos grupos TE e TEQ. A quitosana adicionada ao sistema adesivo não influenciou a permeabilidade dentinária. Conclusões: A estratégia autocondicionante levo

Hancornia speciosa Gomes Latex Increases Bone Mineralization in Rats: A Preclinical Study / Látex de Hancornia speciosa Gomes aumenta a mineralização óssea em ratos: Um estudo pré-clínico

Abstract Objective To evaluate the systemic effect of Hancornia speciosa latex on bone neoformation and mineralization in rats. Methods For that, the latex was first collected, and its composition was analyzed. A total of 30 male Wistar rats were used, which were simultaneously submitted to two surgical procedures: extraction of an incisor and creation of a defect with 2 mm in diameter in the parietal bone. The rats were divided into two groups: systemic control (SC) systemic latex (SX) which were administered, orally and daily, 1.5 mL of water or a solution containing 50% of water and 50% of latex by gavage, respectively. After 15 days of the treatment, the animals were euthanized and their samples were collected. Results The results were statistically analyzed, and the level of significance was set at 0.05. We showed that H. speciosa latex contained calcium. The oral and daily administration of the latex for 15 days increased the contents of calcium and phosphorus in the basal bone and newly-formed bone in the mandibular alveolus of rats. Conclusion The present was a pioneer study demonstrating the potential of H. speciosa latex in increasing bone mineralization. Our results may aid in the conception and development of a natural drug.

Resumo Objetivo Avaliar o efeito sistêmico do látex de Hancornia especiosa na neoformação óssea e mineralização em ratos. Métodos Para isso, primeiro o látex foi coletado, e sua composição foi analisada. No estudo, foram utilizados 30 ratos Wistar machos submetidos simultaneamente a dois procedimentos cirúrgicos: extração de incisivo e criação de um defeito de 2 mm de diâmetro no osso parietal. Os ratos foram divididos em dois grupos: controle sistêmico (CS) e látex sistêmico (XS), aos quais foi administrado, oral e diariamente, 1,5 mL de água ou uma solução contendo 50% de água e 50% de látex por gavagem, respectivamente. Após 15 dias do tratamento, os animais foram eutanizados, e suas amostras, coletadas. Resultados Os resultados foram analisados estatisticamente, e o nível de significância foi fixado em 0,05. Mostramos que o látex de H. speciosa continha cálcio. A administração oral e diária deste látex por 15 dias aumentou o conteúdo de cálcio e fósforo de osso basal e de osso recém-formado no alvéolo mandibular de ratos. Conclusão Este foi um estudo pioneiro, que demonstrou o potencial do látex de H. speciosa no aumento da mineralização óssea. Nossos resultados podem ajudar na concepção e no desenvolvimento de uma droga natural.

Microbiological and microstructural analysis of indwelling bladder catheters and urinary tract infection prevention / Análisis microbiológico y microestructural de sondas vesicales permanentes y prevención de infecciones del tracto urinario / Análise microbiológica e microestrutural dos cateteres vesicais de demora e prevenção de infecção do trato urinário

ABSTRACT Objective: To analyze the microbiological and microstructural part of indwelling urinary catheters and their association with urinary tract infection prevention. Method: This is a cross-sectional study, from June to December 2020, in which 42 indwelling urinary catheter tips and sterile urine samples were collected for analysis of crystals in optical microscopy and biofilms in scanning electron microscopy. Culture analysis and specification of the type of bacteria were performed. Results: It was found that 35.71% of the samples had mature biofilm adhered to the catheter tip. Biofilms of Proteus mirabilis, Enterococcus faecalis, Staphylococcus epidermidis, Enterococcus faecium and Enterobacter cloacae stood out. The presence of magnesium-ammonium-phosphate crystal was associated with the presence of urinary tract infection and with Proteus mirabilis. There was a significant association (p = 0.001) between the use of prophylactic antibiotics versus urine culture >105 CFU/mL. Conclusion: The analyzes contributed to clinical practice, as it reinforces the development of effective and monitored strategies on cultures and urinary tract infection prevention associated with indwelling urinary catheters.

RESUMEN Objetivo: Analizar la parte microbiológica y microestructural de los catéteres urinarios permanentes y su asociación con la prevención de la infección del tracto urinario. Método: Transversal, de junio a diciembre de 2020, en el que se recolectaron 42 puntas de sonda urinaria permanente y muestras de orina estéril para análisis de cristales en microscopía óptica y biopelículas en microscopía electrónica de barrido. Se realizaron análisis de cultivo y especificación del tipo de bacteria. Resultados: Se encontró que el 35,71% de las muestras presentaban biopelícula madura adherida a la punta del catéter. Se destacaron las biopelículas de Proteus mirabilis, Enterococcus faecalis, Staphylococcus epidermidis, Enterococcus faecium y Enterobacter cloacae. La presencia de cristales de fosfato de magnesio-amonio se asoció con la presencia de infección del tracto urinario y con Proteus mirabilis. Hubo una asociación significativa (p = 0,001) entre el uso de antibióticos profilácticos versus urocultivo >105 UFC/mL. Conclusión: Los análisis contribuyeron a la práctica clínica, ya que refuerzan el desarrollo de estrategias efectivas y monitoreadas sobre cultivos y prevención de la infección del tracto urinario asociada a los catéteres urinarios permanentes.

RESUMO Objetivo: Analisar a parte microbiológica e microestrutural dos cateteres vesicais de demora e sua associação com a prevenção de infecção do trato urinário. Método: Transversal, entre junho e dezembro de 2020, em que foram coletadas 42 pontas cateteres vesicais de demora e amostras de urina estéril para análise de cristais em microscopia óptica e de biofilmes em microscopia eletrônica de varredura. Fez-se analise de cultura e especificação do tipo de bactérias. Resultados: Verificou-se que 35,71% das amostras apresentaram o biofilme maduro aderido à ponta do cateter. Destacaram-se biofilmes de Proteus mirabilis, Enterococcus faecalis, Staphylococcus epidermidis, Enterococcus faecium e Enterobacter cloacae. A presença do cristal magnésio-amônio-fosfato foi associada à presença de infecção do trato urinário e ao Proteus mirabilis. Verificou-se associação significativa (p = 0,001) entre o uso de antibiótico profilático versus a urocultura >105 UFC/mL. Conclusão: As análises contribuíram para a prática clínica, pois reforçam a elaboração de estratégias efetivas e monitoradas sobre culturas e prevenção de infecção do trato urinário associada ao cateter vesical de demora.

Efeito do acabamento e polimento sobre a topografia superficial de uma resina composta convencional e uma bulk fill / Effect of finishing and polishing on the surface topography of a conventional compound resin and a bulk fill / Efecto de acabado y pulido en la topografía superficial de una resina compuesta convencional y un llenado a granel

Introdução:As atuaisresinas Bulk-Fill apresentamcomovantagens e propriedades: menor tempo clínico, baixa contração de polimerização, maior translucidez, entre outros. Objetivo:Avaliar a topografia superficial de restaurações com diferentes tipos de resina composta antes e após submetê-las a diferentes sistemas de acabamento e polimento. Metodologia:Confecção de100 corpos de prova, sendo 50 de cada composto resinoso, apresentando cinco grupos (n=10) sorteados de forma aleatória, de acordo com o sistema de acabamento e polimento empregado. Foram utilizadas as resinas Filtek Z350 XT e a Bulk Fill Filtek One Bulk Fill e os sistemas de acabamento e polimento: Discos de Lixa Sof-Lex Pop On Kit;Discos Diamantado Espiral Sof-Lex; Ponta Enhance e Broca Carbide Multilaminada nº 0283F, que foram comparados com superfície deixada pela Tira de Poliester (Controle Negativo). Após 7 dias de armazenamento em água destilada, os corpos de provaforam submetidos aoMicroscópio Eletrônico de Varredura.Resultados:Os corpos de provada resina Bulk Fill tiveram como melhor resultado o sistema de acabamento e polimentocom broca carbidee resultado não satisfatório com discodiamantado espiral Sof-lex, enquanto a ponta Enhance e lixa Sof-lex Pop Ontiveram resultados semelhantes. Os corpos de prova da resina Filtek Z350 XT tiveram melhor aspecto visual de lisura no grupo controle negativoe pior resultado no grupo com disco diamantado espiral Sof-lex. Conclusões:Dessa forma, o sistema que apresentou melhor resultado foi a broca Carbidena resina Bulk Fill, enquanto a Filtek Z350 XT apresentou-se melhor no grupo controle. Porém, ainda são necessáriosestudos para se chegar em um protocolo de acabamento e polimento mais eficiente (AU).

Introduction:The current Bulk-Fill resins have the following advantages and properties: less clinical time, low polymerization shrinkage, greater translucency, among others.Objective:Toevaluate the topography of restorations with different types of composite resin before and after submitting them to different finishing and polishing systems.Methodology:Manufacture of 100 specimens, 50 of each resin compound, presenting five groups (n = 10) drawn at random, according to the finishing and polishing system employed. Filtek Z350 XT resins and Bulk Fill Filtek One Bulk Fill andfinishing and polishing systems were used: Sof-Lex Pop On Kit Sanding Discs; Diamond Spiral Sof-Lex Discs; Tip Enhance and Multilaminated Carbide Drill nº 0283F, which were compared with the surface left by the Polyester Strip (Negative Control). After 7 days of storage in distilled water, the specimens were submitted to a Scanning Electron Microscope.Results:The Bulk Fill resin specimens had the best result of the finishing and polishing system with carbide drill and unsatisfactory result with Sof-lex spiral diamond disc, while the Enhance tip and Sof-lex Pop On sandpaper had similar results. The Filtek Z350 XT resin specimens had a better visual aspect of smoothness in the negative control group and a worse result in the group with Sof-lex spiral diamond wheel.Conclusions:Thus, the system that showed the best result was the Carbide drill in Bulk Fill resin, while Filtek Z350 XT was better in the control group. However, studies are still needed to arrive at a more efficient finishing and polishing protocol (AU).

Introducción:Las actuales resinas Bulk-Fill tienen las siguientes ventajas y propiedades: menor tiempo clínico, baja contracción de polimerización, mayor translucidez, entre otras.Objetivo: Evaluar la topografía de restauraciones con diferentes tipos de resina compuesta antes y después de someterlas a diferentes sistemas de acabado y pulido.Metodología: Fabricación de 100 probetas, 50 de cada resina compuesta, presentando cinco grupos (n = 10) extraídos al azar, según el sistema de acabado y pulido empleado. Se utilizaron resinas Filtek Z350 XT y Bulk Fill Filtek One Bulk Fill y sistemas de acabado y pulido: Discos de lijado Sof-Lex Pop On Kit; Discos Sof-Lex en espiral de diamante; Broca Realce de Punta y Carburo Multilaminado nº 0283F, que fueron comparadas con la superficie dejada por la Tira de Poliéster (Control Negativo). Después de 7 días de almacenamiento en agua destilada, lasmuestras se sometieron a un Las muestras de resina Bulk Fill tuvieron el mejor resultado del sistema de acabado y pulido con broca de carburo y un resultado insatisfactorio con el disco de diamante en espiral Sof-lex, mientras que la punta Enhance y el papel de lija Sof-lex Pop On tuvieron resultados similares. Las muestras de resina Filtek Z350 XT tuvieron un mejor aspecto visual de suavidad en el grupo de control negativo y un peor resultado en el grupo con disco de diamante en espiral Sof-lex.Conclusiones: Así, el sistema que mejor resultado mostró fue la broca Carbide en resina Bulk Fill, mientras que Filtek Z350 XT fue mejor en el grupo control. Sin embargo, aún se necesitan estudios para llegar a un protocolo de acabado y pulido más eficiente (AU).

Silicon-enriched hydroxyapatite formed induced by REFIX-based toothpaste on the enamel surface / Formação de hidroxiapatita enriquecida com silício induzida por dentifrício à base de REFIX na superfície do esmalte

Objetivo: Este estudo in vitro objetivou caracterizar o teor de minerais e a morfologia das partículas de um dentifrício fluoretado contendo tecnologia REFIX e o teor de minerais e a morfologia da superfície do esmalte tratada com este produto. Material e Métodos: Blocos de esmalte bovino (n=5) foram obtidos (4×4×6 mm), desmineralizados (lesão de cárie artificial) e tratados (ciclagem de pH e escovação com dentifrício). Durante a ciclagem de pH de 7 dias (desmineralização e remineralização levaram 6 h e 18 h, respectivamente), o esmalte foi escovado por 5 min com uma escova dental elétrica antes de ser imerso em uma solução de remineralização. Avaliou-se a micromorfologia e os níveis elementares (% em peso) dos íons presentes no dentifrício e na camada formada sobre o esmalte após o tratamento. A morfologia da superfície foi avaliada por meio de microscopia eletrônica de varredura (MEV). As análises elementares foram realizadas usando um espectrômetro de energia dispersiva de raios-X (EDS). Resultados: A análise por MEV do dentifrício demonstrou uma distribuição de tamanho uniforme de partículas de forma regular que foram organizados esparsamente em "nanoclusters". A análise elementar da formulação do dentifrício demonstrou a presença de Si (silício), Na (sódio), P (fósforo) e F (flúor), entre outros. Observou-se também uma camada mineral na superfície de esmalte com espessura uniforme consistente em torno de 14 µm. Conclusão: De acordo com os resultados, conclui-se que a tecnologia REFIX modifica a superfície e subsuperfície da estrutura do esmalte, formando uma camada mineral rica em silício. (AU)

Objective: This in vitro study aimed at characterizing the mineral content and filler particle morphology of a fluoridated toothpaste containing REFIX technology and the mineral content and the morphology of the enamel surface treated with this product. Material and Methods: Bovine enamel blocks (n=5) were obtained (4×4×6 mm), demineralized (artificial caries lesion), and treated (pH cycling and brushing with the toothpaste). During the pH cycling, which lasted for 7 days (demineralization and remineralization took 6 h and 18 h, respectively), the enamel was brushed for 5 min using an electric toothbrush before being immersed in a remineralization solution. We evaluated the micromorphology and elemental levels (wt%) of ions present in the toothpaste and on the layer formed over the enamel following the treatment. The surface morphology was assessed using scanning electron microscopy (SEM). The elemental analyses were performed using an energy-dispersive X-ray spectrometer (EDS). Results: Scanning electron micrographs of the toothpaste demonstrated a uniform size distribution of regular-shaped fillers sparsely organized in nanoclusters. Elemental analysis of the toothpaste's formulation demonstrated the presence of Si (silicon), Na (sodium), P (phosphorus), and F (fluorine), among others. We also detected a mineral layer that had formed on the treated enamel surface; the layer had a consistent uniform thickness of ~14 µm. Conclusion: Based on the results, it can be stated that REFIX technology modifies the surface and subsurface of the enamel structure, forming a Si-rich mineral layer. (AU)

Analysis of the association of parameters in the formation of ultrafine fibers from PEI and PMMA / Análise da associação de parâmetros na formação de fibras ultrafinas de PEI e PMMA

Objective: The aim of the study was to fabricate and morphologically characterize ultrafine Polyetherimide fibers (PEI) associated with Polymethylmethacrylate (PMMA) ­ PP (group formed by the association of PEI with PMMA), produced by the electrospinning process. Material and Methods: A solution of PEI (0.562 g) + PMMA (0.377 g) dissolved in 2.5 mL of chloroform, 0.85 mL of Dimethylformamide (DMF) and 0.85 mL of 1.1.2.2 Tetrachloroethane (TCE) was prepared. For the electrospinning process, different continuous voltages (10 to 18 kV) and two different distances (8 and 12 cm) between the needle tip and the collecting apparatus were used, giving rise to 6 distinct groups of ultrafine fibers (PP 1 to 6) that were observed in Scanning Electron Microscopy to check for defects and calculate the average diameter of the fibers. Results: The best parameter, the parameter that was most effective for the production of fibers, observed was subjected to Energy Dispersion X-ray Spectroscopy (EDS), X-ray Diffraction (XRD) and Contact Angle Analysis tests. The data were analyzed using the ANOVA and Tukey test (p <0.05). From the comparative analysis of the pre-established parameters, the pattern of PP4 ultrafine fibers was shown to be more effective. Conclusion: The PP4 standard (13 kV ­ 12 cm) had an average diameter of 0.37 µm. An adequate parameter to electrospinning was able to produce ultrafine fibers of PMMA/PEI (AU)

Introdução: O objetivo do estudo foi sintetizar e caracterizar morfologicamente fibras ultrafinas de Polieterimida (PEI) associadas ao Polimetilmetacrilato (PMMA) - PP (grupo formado pela associação de PEI com PMMA), produzidas pelo processo de eletrofiação. Material e Métodos: Foi preparada uma solução de PEI (0,562 g) + PMMA (0,377 g) dissolvido em 2,5 mL de clorofórmio, 0,85 mL de Dimetilformamida (DMF) e 0,85 mL de 1.1.2.2 Tetracloroetano (TCE). Para o processo de eletrofiação, foram utilizadas diferentes tensões contínuas (10 a 18 kV) e duas distâncias diferentes (8 e 12 cm) entre a ponta da agulha e o aparelho coletor, dando origem a 6 grupos distintos de fibras ultrafinas (PP 1 a 6) que foram observados em Microscopia Eletrônica de Varredura para verificar defeitos e calcular o diâmetro médio das fibras. Resultados: O melhor parâmetro, o parâmetro mais eficaz para a produção de fibras, observado foi submetido aos testes de Espectroscopia de Dispersão de Energia (EDS), Difração de Raios X (DRX) e Análise do Ângulo de Contato. Os dados foram analisados pela ANOVA e teste de Tukey (p <0,05). A partir da análise comparativa dos parâmetros pré-estabelecidos, o padrão das fibras ultrafinas PP4 mostrou-se mais eficaz. Conclusão: O padrão PP4 (13 kV - 12 cm) apresentou diâmetro médio de 0,37 µm. Um parâmetro adequado para eletrofiação foi capaz de produzir fibras ultrafinas de PMMA / PEI. (AU)

Avaliação das características superficiais dos instrumentos Reciproc, Reciproc Blue e Xp-Endo Shaper / Evaluation of the surface characteristics of the Reciproc, Reciproc Blue and Xp-Endo Shaper instruments

Introdução: o controle da qualidade no processo de fabricação dos instrumentos endodônticos é importante uma vez que defeitos e falhas superficiais podem comprometer o preparo dos canais. Objetivo: avaliar a presença de defeitos e falhas do processo de fabricação na superfície de instrumentos Reciproc (R25), Reciproc Blue (RB25) e XP-endo shaper (XP), por meio de microscopia eletrônica de varredura (MEV). Materiais e Métodos: Ao total, foram avaliados 60 instrumentos de níquel titânio, sendo 20 por grupo: R25, RB25 e XP, em três regiões: 0mm (ponta do instrumento), 4mm e 7mm da ponta, no MEV, com aumento de 100x. As imagens foram avaliadas quanto ao número de falhas de fabricação (bordo irregular, ranhura, microcavidade e rebarba) e por um sistema de escores de 1 a 4, sendo 1, nenhuma área com defeito e 4, mais de cinco áreas com defeitos na superfície. Os dados foram submetidos à análise estatística utilizando o teste de Dunn (p<0,05). Resultados: Sobre a análise por regiões, foram identificadas diferenças significativas em grande parte dos instrumentos. Comparando os diferentes instrumentos, não foi observada diferença significativa para microcavidade (p=0,76), bordo irregular (p=0,98) e rebarba (p=0,40). O instrumento R25 mostrou maior número de ranhuras em comparação aos demais (p=0,0000*). RB25 mostrou maiores valores de escores que os instrumentos R25 (p= 0,0002) eXP (p=0,01). Conclusão: Todos os instrumentos avaliados apresentaram defeitos/falhas superficiais do processo de fabricação.

Introduction: The quality control of endodontic instruments is extremely importantsince defects and failures on their surface, during their manufacturing process, can compromise the preparation of root canal. Objective: this study evaluated the presence of defects and failures in the manufacturing process on the surface of Reciproc (R25), Reciproc Blue (RB25) and XP endo-shaper (XP) instruments by means of scanning electron microscopy (SEM). Materials and Methods: In total, sixty nickel titanium instruments (n=20): R25, RB25 and XP were evaluated in the scanning electron microscope in three regions: 0mm (tip of the instrument), 4mmand 7mm of the tip, with a magnification of 100x. The images were evaluated in relation to the number of manufacturing faults (irregular border, groove, microcavity and burr) and by a system of scores, from 1 to 4, where 1 is no defective area and 4, more than five areas with defects on the surface. The data were submitted to statistical analysis using Kruskal-Wallis and Mann-Whitney tests (p<0.05). Results: Regarding the analysis by regions, significant differences were identified in most of the instruments. Comparing the different instruments, no significant difference was observed for microcavity (p=0.76), irregular border (p=0.98) and burr (p=0.40). The R25 instrument showed a greater number of grooves compared to the others (p=0.0000*). RB25 showed higher scores than the R25(p=0.0002) and XP (p=0.01) instruments. Conclusion: All evaluated instruments showed defects/failures in the manufacturing process.Introduction: The quality control of endodontic instruments is extremely importantsince defects and failures on their surface, during their manufacturing process, can compromise the preparation of root canal. Objective: this study evaluated the presence of defects and failures in the manufacturing process on the surface of Reciproc (R25), Reciproc Blue (RB25) and XP endo-shaper (XP) instruments by means of scanning electron microscopy (SEM). Materials and Methods: In total, sixty nickel titanium instruments (n=20): R25, RB25 and XP were evaluated in the scanning electron microscope in three regions: 0mm (tip of the instrument), 4mmand 7mm of the tip, with a magnification of 100x. The images were evaluated in relation to the number of manufacturing faults (irregular border, groove, microcavity and burr) and by a system of scores, from 1 to 4, where 1 is no defective area and 4, more than five areas with defects on the surface. The data were submitted to statistical analysis using Kruskal-Wallis and Mann-Whitney tests (p<0.05). Results: Regarding the analysis by regions, significant differences were identified in most of the instruments. Comparing the different instruments, no significant difference was observed for microcavity (p=0.76), irregular border (p=0.98) and burr (p=0.40). The R25 instrument showed a greater number of grooves compared to the others (p=0.0000*). RB25 showed higher scores than the R25(p=0.0002) and XP (p=0.01) instruments. Conclusion: All evaluated instruments showed defects/failures in the manufacturing process.

Eficácia de três protocolos de irrigação final para remoção de raspas dentinárias e material obturador em irregularidades simuladas / Effectiveness of three final irrigation protocols for debris and filling removal from simulated irregularities

Objetivos: Avaliar três protocolos de irrigação final para remoção de detritos e material obturador de istmos simulados. Métodos: Setenta e oito pré-molares foram preparados com o sistema WaveOne Gold 45.05. Os dentes foram seccionados longitudinalmente e um istmo padronizado foi confeccionado no terço apical. Seis raízes foram utilizadas como controle negativo. Os espécimes foram randomizados em dois grupos principais (n=36). Trinta e seis raízes tiveram o istmo preenchido com detritos e as outras trinta e seis raízes foram obturadas com guta-percha e cimento endodôntico, por meio da técnica híbrida de Tagger. Cada grupo foi dividido em três subgrupos (n=12), de acordo com o protocolo de irrigação final: Easy Clean; irrigação ultrassônica passiva (PUI); e XP Clean. A ativação do NaOCl 2,5% pelo Easy Clean foi realizada em três ciclos de vinte segundos; e pelo XP Clean, por um minuto em movimento reciprocante e contínuo, respectivamente. No grupo PUI, o irrigante foi ativado em três períodos de vinte segundos. Resultados: Não foi encontrada associação entre os escores de remoção de detritos e os protocolos de irrigação (p=0,165). Foi observada associação entre os escores de remoção do material obturador e os protocolos de irrigação final (p<0,05). Conclusões: Os protocolos de irrigação final foram efetivos para a remoção de detritos, mas não para remoção de material obturador de istmos no terço apical (AU).

This study aimed to assess three final irrigation protocols on debris and filling removal from simulated irregularities. Methods: Seventy-eight mandibular premolars were prepared with WaveOne Gold system 45.05, splitted longitudinally, and a standardized groove was performed in the apical portion of the canals. Six roots served as negative control. The roots were randomly divided into two main groups (n = 36). The grooves were filled with dentin debris in thirty six roots. The others thirty-six were filled with gutta-percha and endodontic sealer using Tagger hybrid technique. Each main group was then divided into three groups (n = 12) according to the final irrigation protocol: Easy Clean, passive ultrasonic irrigation (PUI), and XP Clean. In Easy Clean 2.5% NaOCl activation was performed for 3 cycles of 20 seconds and XP Clean for one minute under reciprocating and continuous rotary motion and continuous rotary motion, respectively. In the PUI group, the irrigant was activated in three periods of 20 seconds. Results: No association was found among the scores of debris removal and the irrigation protocols (p = .165). An association was observed among the filling material removal scores and irrigation protocols (p< .05). Conclusion: Easy Clean, PUI and XP Clean were effective for dentin debris removal, but did not for filling material from artificial grooves in the apical third (AU).

Microtensile Bond Strength and Failure Type Analysis of Self-Etch Adhesive Systems on Superficial and Deep Dentin After Long-term Water Storage / Análise de resistência de adesão à microtração e tipo de falha de sistemas adesivos autocondicionantes em dentina superficial e profunda após armazenamento longitudinal em água

Objective: The aim of this study was to evaluate and compare the microtensile bond strengths of four current adhesive materials that contain different monomers at deep and superficial dentin. Material and Methods: Forty non-carious human third molars (n=5) were used in the study. Specimens were divided into two main groups according to dentin thickness as superficial and deep dentin. Groups were further divided into four subgroups in terms of the adhesive systems used: Nova Compo B Plus (NCBP), Nova Compo B (NCB), Futurabond M (FB) and Clearfil S3 Bond Plus (CS3). All specimens were bonded to resin composite and stored in 37 °C water for 9-months. Teeth were sectioned into 3 x 3 mm thick beams. Microtensile bond strength test was carried out by using a universal testing device (1 mm/min). After fracture, failure types were observed using an optical microscope and the fractured dentin surfaces were observed by a scanning electron microscopy (SEM). One-way ANOVA and Tukey tests were used to compare the adhesive system in each dentin group. An unpaired T-test was used to compare the dentin thickness in each adhesive material. Results: As compared to deep dentin, superficial dentin showed higher µTBS values in groups NCBP, FB and CS, as opposed to group NCB. Only NCB revealed higher bond strength at deep dentin layers when compared to superficial dentin. In the superficial dentin group, NCBP showed the highest bond strength value while NCB showed the lowest bond strength. In the deep dentin group, while NCB showed the highest bond strength value, NCBP revealed the lowest bond strength value after 9-months storage. While 4-META and 10-MDP monomer combination (NCBP) resulted in the highest bond strength value among the adhesive systems in the superficial dentin group, the GPDMA and 4-META monomer combination (NCB) resulted in the highest bond strength in deep dentin group. Conclusions: Microtensile bond strength performance are affected by both the type of monomer in the adhesive combination and the depth of the dentin. (AU)

Objetivo: o objetivo deste estudo foi avaliar e comparar a resistência de união à microtração de quatro materiais adesivos atuais que contêm monômeros diferentes na dentina profunda e superficial. Material e Métodos: Quarenta terceiros molares humanos não cariados (n = 5) foram usados no estudo. Os espécimes foram divididos em dois grupos principais de acordo com a espessura da dentina em superficial e profunda. Os grupos foram subdivididos em quatro subgrupos quanto aos sistemas adesivos usados: Nova Compo B Plus (NCBP), Nova Compo B (NCB), Futurabond M (FB) e Clearfil S3 Bond Plus (CS3). Todos os espécimes foram aderidos à resina composta e armazenados em água a 37 ° C por 9 meses. Os dentes foram seccionados em palitos de 3 x 3 mm de espessura. O teste de microtração foi realizado com o uso de um dispositivo de teste universal (1 mm / min). Após a fratura, os tipos de falha foram observados em microscópio óptico e as superfícies de dentina fraturadas por microscopia eletrônica de varredura (MEV). Os testes ANOVA e Tukey um fator foram usados para comparar o sistema adesivo em cada grupo de dentina. Um teste T não pareado foi usado para comparar a espessura da dentina em cada material adesivo. Resultados: Em comparação com a dentina profunda, a dentina superficial apresentou maiores valores de µTBS nos grupos NCBP, FB e CS, ao contrário do grupo NCB. Apenas NCB revelou maior resistência de união na dentina profunda quando comparada à dentina superficial. No grupo de dentina superficial, NCBP apresentou o maior valor de resistência de união, enquanto NCB apresentou a menor resistência de união. No grupo de dentina profunda, enquanto NCB apresentou o valor de resistência de união mais alto, NCBP revelou o valor de resistência de união mais baixo após 9 meses de armazenamento. Enquanto a combinação de monômero 4-META e 10-MDP (NCBP) resultou no maior valor de resistência de união entre os sistemas adesivos no grupo de dentina superficial, a combinação de monômero (NCB) resultou na maior força de união no grupo de dentina profunda. Conclusões: O desempenho da resistência de união à microtração é afetado tanto pelo tipo de monômero na combinação adesiva quanto pela profundidade da dentina. (AU)

Avaliação da interface entre o componente protético reto e a conexão interna tipo Cone Morse do implante dentário por meio da microscopia eletrônica de varredura / Evaluation of the interface between the straight prosthetic component and the Morse Cone-type internal connection of the dental implant in cross section by scanning electron microscopy

Resumo Introdução A interface implante-pilar protético e a formação dos seus microgaps são aspectos relevantes na transferência das cargas e na resposta biológica, estando ligadas ao sucesso da reabilitação. Objetivo Avaliar microgaps na interface entre a conexão interna do implante do tipo Cone Morse e a superfície do componente protético por meio da microscopia eletrônica de varredura (MEV). Material e método Foram utilizados 20 implantes dentários de tamanho 3,75 × 11,0mm do tipo Cone Morse com seus respectivos pilares protéticos da Singular® (Singular Implants, RN, Brasil). Os munhões retos foram acoplados aos implantes com torque de 32N/cm2 e o conjunto resultante foi emergido em base de Resina Epóxi ES260, para permitir secção longitudinal da amostra. As amostras foram analisadas e os microgaps mensurados no MEV (JEOL JCM-5700, MA, USA), e posteriormente os dados foram analisados. Resultado A média e o desvio padrão dos maiores microgaps foram observados na parte apical do implante nos lados direito e esquerdo, sendo 1,44±2,68 e 1,16±1,49 μm, respectivamente. Os menores microgaps foram na parte superior do implante nos lados direito e esquerdo, sendo 0,60±0,73 e 0,66±0,67 μm, respectivamente. Contudo, no teste de Kruskal-Wallis, não houve diferença estatisticamente significativa entre as regiões dos implantes, tanto para o lado esquerdo (p=0,692) como para o direito (p=0,865). No teste de Mann-Whitney, não houve diferenças estatisticamente significativas entre os lados para as diferentes regiões dos implantes. Conclusão Mesmo com a presença de microgaps na interface implante-pilar protético, estes apresentam tamanho inferior ao que causaria problemas biológicos e mecânicos. As amostras analisadas quanto à sua compatibilidade de encaixe foram satisfatórias.

Abstract Introduction The implant-prosthetic abutment interface and the formation of its microgaps are relevant aspects in load transfer and biological response and are linked to the success of the rehabilitation. Objective To evaluate microgaps at the internal connection interface of the Cone Morse implant and the prosthetic component surface by means of scanning electron microscopy (SEM). Material and method Twenty 3.75 x 11.0 mm Cone Morse dental implants with their respective Singular® prosthetic abutments were used (Singular Implants, RN, Brazil). The straight trunnions were attached to the implants with a 32N/cm2 torque and the ES260 Epoxy Resin-based set emerged to allow longitudinal sectioning of the sample. The samples were analyzed and the microgaps measured in SEM (JEOL JCM-5700, MA, USA), and later the data were analyzed. Result The mean and standard deviation of the largest microgaps were observed in the apical part of the right and left side 1.44±2.68 and 1.16±1.49 μm, respectively. The smallest microgaps were on the upper implant right and left sides 0.60±0.73 and 0.66±0.67 μm, respectively. However, in the Kruskal-Wallis test there was no statistically significant difference between the implant regions, both for the left side (p=0.692) and right side (p=0.865). The Mann-Whitney test, there were no statistically significant differences between the sides for the different regions of the implants. Conclusion Even with the presence of microgaps in the implant-post interface, it presents a smaller size than the one presenting biological and mechanical problems. The samples analyzed for their fitting compatibility were satisfactory.

Chemical and structural composition of black pigmented supragingival biofilm of bovines with periodontitis / Composição química e estrutural do biofilme supragengival pigmentado de bovinos com periodontite

Bovine periodontitis is a multifactorial disease primarily associated with a potentially pathogenic microbiota housed in the oral biofilm of animals. Biofilms are organized structures, in which the constituents coexist in symbiosis, already described as a predisposing factor to periodontitis in other species. The objective of the present study was to characterize the structure and chemical aspects of the bovine black pigmented supragingival biofilm using scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS), respectively, and determine its relationship with bovine periodontitis. Eleven premolar teeth from different animals were evaluated; five non-pigmented samples and six samples with black pigmented biofilms were initially submitted to SEM, and three areas of these samples were selected for EDS. The structure of the pigmented biofilm was more complex and irregular because of a higher content of mineral elements. The semi-quantitative EDS data indicated an association of iron (p<0.014) and magnesium (p<0.001) with the occurrence of periodontitis, whereas carbon, phosphorus, calcium, manganese, sodium, and potassium were not associated with the disease. Carbon (p<0.039), manganese (p<0.007), and iron (p<0.015) were associated with pigmentation, whereas phosphorus, calcium, and magnesium were not associated with it. Spearman correlation test showed the relationships between calcium and phosphorus, and iron and silicon. The strong association of iron in the pigmented supragingival biofilm and with the occurrence of periodontitis suggests the presence of microorganisms that use this element in their metabolism and that are also associated with bovine periodontitis. This study suggests that the pigmented deposits in the crown of the teeth of cattle are an true biofilm with the deposition of iron, and it indicates that the presence of iron and magnesium in these formations may be involved in the metabolism of some microorganisms associated with the etiology of bovine periodontitis.(AU)

A periodontite bovina é uma infecção multifatorial associada primariamente à microbiota potencialmente patogênica presente no biofilme bucal. Biofilmes são estruturas organizadas, nas quais os constituintes convivem em simbiose, descritos em outras espécies como um fator predisponente à periodontite. O objetivo do presente estudo foi caracterizar estrutural e quimicamente o biofilme supragengival pigmentado de preto em bovinos, utilizando-se as técnicas de microscopia eletrônica de varredura (MEV) e espectroscopia de dispersão de energia (EDS), respectivamente, correlacionando os elementos identificados à ocorrência de periodontite e pigmentação. Foram avaliados 11 dentes primeiro-molares; cinco amostras sem pigmentação visível e seis amostras com biofilme pigmentado de preto, que foram submetidas inicialmente à MEV; posteriormente foram selecionadas três áreas aleatórias de cada dente para realização da EDS. A estrutura do biofilme pigmentado revelou formações irregulares e mais complexas, provavelmente devido ao maior acúmulo de elementos minerais. Os resultados semi-quantitativos da EDS apontaram associações entre a presença de ferro (p<0,014) e magnésio (p<0,001) com a ocorrência de periodontite. Carbono, fósforo, cálcio, manganês, sódio e potássio não apresentaram associação com a periodontite. Em relação à pigmentação, carbono (p<0,039), manganês (p<0,007) e ferro (p<0,015) foram os elementos estatisticamente significantes, enquanto fósforo, cálcio e magnésio não apresentaram associação com a pigmentação. O teste de correlação de Spearman demonstrou associações entre os elementos cálcio e fósforo, e ferro e silício. A forte associação do ferro presente no biofilme supragengival com a ocorrência de periodontite, sugere a presença de micro-organismos que utilizam este elemento em seu metabolismo e que possivelmente tenham envolvimento com o desenvolvimento da periodontite bovina. Os resultados inéditos do presente trabalho sugerem que os depósitos pigmentados que se formam na coroa dos dentes de bovinos são um biofilme verdadeiro com deposição de ferro, e indicam que a presença de ferro e magnésio nestas formações pode estar envolvida no metabolismo de alguns dos principais micro-organismos associados à etiologia da periodontite bovina.(AU)

Estudo das propriedades físicas de um biomaterial com nova composição de wollastonita e beta fosfato tricálcico para regeneração óssea após implante in vivo / Study of the physical properties of a biomaterial with a new composition of wollastonite and beta-tricalcium phosphate for bone regeneration after implantation in vivo

Introdução: associadas à composição química, as propriedades físicas dos biomateriais como formato, dimensões e porosidade, são fatores que influenciam na biocompatibilidade, biodegradabilidade e nos potenciais osteoindutivo e osteocondutores. Objetivo: identificar modificações físicas no formato, dimensões e porosidade de um biomaterial com nova composição de wollastonita e beta fosfato tricálcico, implantado em defeitos ósseos críticos em calvária de ratos. Metodologia: trata-se de um estudo exploratório, com um biomaterial compósito, antes e após a sua implantação in vivo. Utilizou-se explantes cirúrgicos de calvárias de ratos que receberam implantes em defeito ósseo crítico. Os animais foram distribuídos em 3 grupos experimentais aleatoriamente, compostos por 5 animais cada, e avaliados com 15, 45 e 120 dias. Os grupos foram denominados: G0-biomaterial; GI-15 dias; GII-45 dias; e, GIII-120 dias. As amostras foram micrografadas em microscópio eletrônico de varredura, com diferentes magnificações. Utilizouse o software livre ImageJ para processamento das imagens e análise das partículas e poros. Resultados: a distribuição espacial do biomaterial promoveu preenchimento completo do defeito ósseo crítico. Micrografias com diferentes magnificações permitiu identificar modificações na área de contato entre grânulos, diminuição dos poros intergranular, aumento da área ocupada pelos poros e diminuição das partículas nos grânulos. Nos grupos GII e GIII, identificou-se formação de componentes orgânicos na superfície do implante. Conclusão: houve modificações físicas no formato, dimensões horizontais, distribuição espacial e porosidade da superfície dos grânulos do biomaterial, relacionadas com a biodegradabilidade e o potencial osteoindutivo e osteocondutor do biomaterial.

Introduction: associated with the chemical composition, physical properties of biomaterials related to their format, dimensions and porosity, are factors that influence on biocompatibility, biodegradability and osteoinductive and osteoconductive potential. Objective: identify physical changes in the format, dimensions and porosity of biomaterial with new composition of wollastonite and beta tricalcium phosphate, implanted in critical bone defects in calvaria of rats. Methodology: this is an exploratory study, with a composite biomaterial before and after its implantation in vivo. Used surgical explants of rat calvarium that received biomaterial implants into the critical bone defect. The animals were divided into 3 experimental groups of random distribution, composed of 5 animals each, and evaluated for 15, 45 and 120 days. The groups were named: G0-Biomaterial; GI-15 days; GII-45 days; and, GIII-120 days. The samples were studied by micrography in scanning electronic microscope with different magnifications. It was used the free software ImageJ to image processing and particles and pores analysis. Results: the spatial distribution of the biomaterial promoted full filling of the critical bone defect. Micrographs with different magnifications allowed to identification of modifications in the area of contact between granules, decrease of the intergranular pores, increase of the area occupied by the pores and decrease of the particles in the granules. In GII, and GIII groups, it was identified formation of organic components on the surface of the implant. Conclusion: there were physical modifications in the format, horizontal dimensions, spatial distribution and porosity of the biomaterial, related to the biodegradability and the osteoinductive and osteoconductive potential of the biomaterial.

Microhardness, Color Stability and Microstructural Analysis of Prefabricated Composite Resin Veneers / Estudo da Microdureza, Estabilidade de cor e Microestrutura de Facetas Pré-Fabricadas de Resina Composta

The aim of the work was to determine Knoop microhardness (KH), color stability (ΔE00) and microstructure of prefabricated composite resin veneers (PCRVs). Two PCRVs systems (Componeer Brilliant New Generation, Coltene, Altstätten, Switzerland; and Direct Veneer, Edelweiss, Wolfurt, Austria) were tested. KH was measured at the buccal surface of the PCRVs. Color analyze was evaluated by a spectrophotometer and ΔE00 calculated using CIEDE2000 formula. Microstructure of the PCRVs was characterized using scanning electron microscopy (SEM). Data of KH and ΔE00 were subjected to One-way ANOVA followed by Tukey post hoc test (α=0.05). Componeer (KH = 46) and Edelweiss (KH = 43) presented statistical similar hardness results (p>0.05). Componeer (ΔE00water= 0.1 and ΔE00coffee= 13.4) showed lower ΔE00 than Edelweiss (ΔE00water= 0.5 and ΔE00coffee= 18.7). SEM-images indicated similar microstructures of the PCRVs tested. Although PCRVs present similar microhardness and microstructure, Componeer showed higher color stability and lower extrinsic pigmentation to coffee in comparison to Edelweiss. Direct composite resin veneer treatment might be simplified with PCRVs. However, the high pigmentation observed in the PCRVs could generate aesthetic failures over the time. (AU)

O objetivo do trabalho foi determinar a microdureza Knoop (KH), estabilidade de cor (ΔE00) e a microestrutura de facetas de resina composta pré-fabricadas. Os sistemas de facetas Componeer e Edelweiss foram testados. Para cada sistema, a microdureza foi avaliada na superfície vestibular das facetas. A análise da estabilidade de cor foi feita mediante o emprego de um espectrofotômetro e a alteração de cor foi calculada seguindo a fórmula determinada pelo CIEDE2000. A microestrutura dos sistemas foi observada e caracterizada a partir de um microscópio eletrônico de varredura. Os resultados de microdureza e alteração de cor foram submetidos a análise de variância de um fator complementados pelo teste de Tukey (α=0,05). Os sistemas de facetas pré-fabricadas de resina composta apresentaram valores estatisticamente similares de microdureza (p>0,05). O grupo Componeer apresentou uma alteração de cor inferior em relação ao grupo Edelweiss. Os dois sistemas apresentaram uma elevada pigmentação após imersão em solução com café. A microestrutura dos sistemas se mostrou similar em função da avaliação das imagens em microscopia. Apesar dos sistemas apresentarem microdureza e microestrutura similares, o sistema Componeer gerou menor alteração de cor com menor pigmentação a bebida corante empregada em comparação ao sistema Edelweiss. A técnica de facetas dentárias pode ser simplificada utilizando um sistema de facetas pré-fabricadas de resina composta. Todavia, a elevada pigmentação observada no presente estudo deve ser levada em consideração já que o tratamento com esse tipo faceta tende a ser um procedimento estético com durabilidade elevada. (AU)

Análise de falhas na superfície ativa de diferentes instrumentos de níquel-titânio por meio da microscopia eletrônica de varredura / Analysis of Failure in the Active Surface of Different Nickel-Titanium Instruments by Scanning Electron Microscopy

Objetivo: Analisar falhas de fabricação na superfície ativa de diferentes instrumentos de níquel-titânio por meio da microscopia eletrônica de varredura. Material e método: Foram analisados um total de 33 instrumentos distribuídos em dois grupos de acordo com a procedência: G1 - Sistema Protaper Next® sendo analisados 03 kits de 05 instrumentos de NiTi cada (X1 ­ 17/0.04; X2 ­ 25/0.06; X3 ­ 30/0.07; X4 ­ 40/0.06; X5 ­ 50.0.06); G2 - Sistema Biorace®, sendo analisados 03 kits constituído de 06 instrumentos cada (BR0 ­ 25/0.08; BR1 ­ 15/0.05; BR2 ­ 25/0.04; BR3 ­ 25/0.06; BR4 ­ 35/0.04; BR5 ­ 40/0.04); Os instrumentos foram retirados da embalagem e direcionados para a análise de falhas na superfície ativa em imagens de microscopia eletrônica de varredura. Para determinação das falhas na superfície do instrumento, dividiu-se a parte ativa de 16mm em 14 partes de 2,55mm cada (S1-S7), nominadas seguimentos de 1 ao 7. Resultados: As frequências de defeitos encontradas para cada segmento dos instrumentos analisados foram cruzadas com os dados do número do instrumento por meio do teste do Qui-quadrado. Houve influência de uma variável sobre a outra apenas quando se analisou o segmento 1 do kit Protaper Next (p=0,005). O instrumento X4 mostrou um número maior de falhas que os demais instrumentos. A relação entre o número de defeitos observados nos diferentes sistemas de instrumentos foi avaliada pelo teste do Qui-quadrado. Não foram encontradas diferenças estatisticamente significantes entre Biorace e Protaper Next (p>0,05). Conclusão: Ambos os instrumentos dos grupos analisados apresentaram algum tipo de falha na superfície ativa.

Aim: To analyze manufacturing failures in the active surface of different nickel-titanium instruments by of scanning electron microscopy. Material and method: A total of 33 instruments distributed in two groups according to the provenance were analyzed: G1 - Protaper Next® System and 03 kits of 05 NiTi instruments were analyzed (X1 - 17 / 0.04; X2 - 25 / 0.06; X3- 30 / 0.07; X4-40 / 0.06; X5-50.0.06); G2 - Biorace® system, with three kits consisting of 06 instruments each (BR0 - 25 / 0.08; BR1 - 15 / 0.05; BR2 - 25 / 0.04; BR3 - 25 / 0.06; BR4 - 35 / 0.04); The instruments were removed and analysis of active surface defects in scanning electron microscopy images. In order to determine the defects on the instrument surface, the active part of 16mm was divided into 14 parts of 2,55mm each (S1-S7), named sequences from 1 to 7. Results: The frequencies of defects found for each segment of instruments were cross-checked with the instrument number data using the chi-square test. There was influence of one variable on the other only when analyzing Segment 1 of the Protaper Next Kit (p = 0.005). Instrument X4 showed more failures than other instruments. The relationship between the number of defects observed in the different instrument systems was evaluated by the chi-square test. No statistically significant differences were found between Biorace and Protaper Next (p> 0.05). Conclusion: Both instruments of the analyzed groups presented some type of fault on the active surface.

Efeito de diferentes protocolos de irrigação final na remoção da smear layer / Effect of different protocols of final irrigation on smear layer removal

Objetivo: esse estudo avaliou o efeito de protocolos de irrigação final, associados ao uso de EDTA e QMix, na remoção de smear layer. Métodos: foram utilizados 40 dentes humanos com canal único. Os canais foram instrumentados com sistema ProTaper Universal SX-F3. As substâncias químicas utilizadas durante o preparo foram hipoclorito de sódio a 5,25% (NaOCl) ou clorexidina a 2% (CHX) gel. Terminado o preparo, os dentes foram divididos em oito grupos, de acordo com os irrigantes: G1) NaOCl 5,25% + EDTA 17% + NaOCl 5,25%; G2) NaOCl 5,25% + EDTA 17% + água destilada (AD); G3) NaOCl 5,25% + QMix + NaOCl 5,25%; G4) NaOCl 5,25% + QMix + AD; G5) CHX 2% gel + EDTA 17% + CHX 2% solução; G6) CHX 2% gel + EDTA 17% + AD; G7) CHX 2% gel + QMix + CHX 2% solução e G8) CHX 2% gel + QMix + AD. As amostras foram avaliadas por microscopia eletrônica de varredura ambiental, antes e após os protocolos de irrigação final. As imagens foram classificadas por escores, em relação à presença de smear layer, e os dados foram analisados pelos testes de Kruskal-Wallis e de Mann-Whitney. Resultados: o G1 mostrou os melhores resultados em relação à remoção de smear layer (p < 0,05). A CHX gel 2% mostrou menor formação de smear layer, quando comparada ao NaOCl, após o preparo biomecânico; e o NaOCl apresentou melhor limpeza como irrigante final (p < 0,05). Conclusões: o NaOCl como irrigante final, combinado ao EDTA, mostrou melhor capacidade de remoção da smear layer (AU).

Introduction: This study evaluated the effect of different final irrigation protocols using EDTA and QMix on smear layer removal. Methods: The root canals of 40 single-rooted human teeth were prepared with ProTaper Universal SX - F3. The substances used were 5.25% sodium hypochlorite (NaOCl), 2% chlorhexidine gel (chlorhexidine), 2% chlorhexidine solution and distilled water. The teeth were divided into 8 groups, according to the irrigant used: G1: 5.25% NaOCl + 17% EDTA + 5.25% NaOCl; G2: 5.25% NaOCl + 17% EDTA + distilled water; G3: 5.25% NaOCl + QMix + 5.25% NaOCl; G4: 5.25% NaOCl + QMix + DW; G5: 2% chlorhexidine gel + 17% EDTA + 2% chlorhexidine solution; G6: 2% chlorhexidine gel + 17% EDTA + distilled water; G7: 2% chlorhexidine gel + QMix + 2% chlorhexidine solution; and G8: 2% chlorhexidine gel + QMix + distilled water. Samples were evaluated under environmental scanning electron microscopy (ESEM) before and after irrigation. ESEM images were classified according to smear layer scores, and the Kruskal-Wallis and Mann-Whitney tests were used for statistical analyses. Results: Group 1 had the best results for smear layer removal (p<0.05). Smear layer formation was lower when 2% chlorhexidine gel was used after cleaning and shaping than when the irrigant was 5.25% NaOCl, and 5.25% NaOCl had the best cleaning ability as a final irrigant. Conclusion: 5.25% NaOCl combined with EDTA was the best final irrigant for smear layer removal (AU).

Avaliação da formação de smear layer no preparo químico mecânico realizado com solução ou gel de hipoclorito de sódio a 2, 5% / Evaluation of smear layer formation in mechanical chemical preparation performed with 2. 5% sodium hypochloride solution or gel

Introdução: a formação de smear layer durante o preparo dos canais radiculares com o uso de hipoclorito de sódio solução já foi amplamente estudada; entretanto, na apresentação em gel não existem relatos na literatura. Objetivo: avaliar, em MEV, a formação de smear layer durante o preparo endodôntico, utilizando o NaOCl nas formas líquida e gel, associado ou não ao EDTA. Métodos: sessenta raízes palatinas de molares superiores ou distais de inferiores, com comprimento radicular padronizado em 15 mm, foram utilizadas. As amostras foram divididas em quatro grupos controle com n = 5 cada (soro fisiológico ou base gel, associados ou não ao EDTA) e quatro grupos testes com n = 10 cada, de acordo com a substância irrigadora empregada durante o preparo (solução ou gel de NaOCl a 2,5%, associados ou não ao EDTA). Os canais foram modelados e posteriormente clivados para análise em MEV (ampliação de 2000x). Imagens de eletromicrografias foram obtidas nos terços cervical, médio e apical. A presença e as características da smear layer formadas foram categorizadas. As imagens foram analisadas por dois avaliadores, previamente, calibrados. Após a análise de concordância (Kappa = 0,806) dos escores, os dados foram tratados com o uso do teste Kruskall-Wallis, complementado pelo teste de Comparações Múltiplas SNK. O nível de significância foi de 5%. Resultados: a utilização do soro fisiológico e do NaOCl líquido, associados à irrigação final com EDTA, apresentou os melhores resultados de limpeza. Com o uso do NaOCl gel e da base gel, sem associação ao EDTA, houve uma maior quantidade de resíduos sobre as paredes dentinárias. Além disso, independentemente da substância irrigadora testada, pode-se observar que houve uma melhor capacidade de remoção da smear layer no terço cervical em relação ao apical. Conclusões: observou-se formação de smear layer após o preparo do canal radicular associado ao NaOCl líquido ou gel. A aplicação de EDTA promoveu a remoção da smear layer produzida durante o preparo do canal.

Introduction: the formation of smear layer during the preparation of root canals with the use of sodium hypochlorite solution has been widely studied; however, in the gel presentation there aren't reports in the literature. Objective: to evaluate, in SEM, the formation of smear layer during endodontic preparation, using NaOCl in liquid and gel forms, associated or not with EDTA. Methods: sixty palatal roots of maxillary molars or distal roots of lower molars, with a root length of 15 mm, were used. The samples were divided into four control groups with n = 5 each (saline or gel base, associated or not with EDTA) and four test groups (n = 10 each) according to the irrigation substance used during the preparation (2.5% NaOCl solution or gel, associated or not with EDTA). The root canals were instrumented and later split for SEM analysis (2000x magnification). Electromicrographic images were obtained from the cervical, middle and apical thirds. The presence and characteristics of the smear layer formed were categorized. The images were analyzed by two previously calibrated evaluators. After the Kappa analysis (0.806), the data were treated using the Kruskall-Wallis test, complemented by the SNK Multiple Comparison Test. The level of significance was 5%. Results: the use of saline and liquid NaOCl, associated with final rinsing with EDTA, showed the best cleaning results. With the use of NaOCl gel and gel base, with no EDTA association, there was a greater amount of residues on the dentin surfaces. In addition, despite the irrigation substance tested, it can be observed that there was a better capacity of removal of the smear layer in the cervical third in relation to the apical. Conclusion: root canal instrumentation associated with NaOCl solution or gel EDTA produced smear layer. Smear layer was removed with the use of EDTA as a final flushing.